[1]李小龍,張軍平,任永峰,等.兩種金屬化合物對喹啉季銨鹽緩蝕性能的影響[J].焊管,2017,40(8):8-11.[doi:10.19291/j.cnki.1001-3938.2017.08.002]
 LI Xiaolong,ZHANG Junping,REN Yongfeng,et al.Influence of Two Kinds of Metal Compounds on Corrosion Inhibition Performance of Quinolone Quaternary Ammonium Salt[J].,2017,40(8):8-11.[doi:10.19291/j.cnki.1001-3938.2017.08.002]
點擊復制

兩種金屬化合物對喹啉季銨鹽緩蝕性能的影響
分享到:

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
40
期數:
2017年第8期
頁碼:
8-11
欄目:
試驗與研究
出版日期:
2017-08-28

文章信息/Info

Title:
Influence of Two Kinds of Metal Compounds on Corrosion Inhibition Performance of
Quinolone Quaternary Ammonium Salt
文章編號:
10.19291/j.cnki.1001-3938.2017.08.002
作者:
李小龍12張軍平3任永峰12晁利寧12苑清英12
1. 國家石油天然氣管材工程技術研究中心, 陜西 寶雞 721008;
2. 寶雞石油鋼管有限責任公司 鋼管研究院, 陜西 寶雞 721008;
3. 西北工業大學 理學院應用化學系, 西安 710129
Author(s):
LI Xiaolong12 ZHANG Junping3 REN Yongfeng12 CHAO Lining12 YUAN Qingying12
1. Chinese National Engineering Research Center for Petroleum and Natural Gas Tubular Goods, Baoji 721008, Shaanxi, China;
2. Steel Pipe Research Institute, Baoji Petroleum Steel Pipe Co., Ltd., Baoji 721008, Shaanxi, China;
3. Department of Applied Chemistry, School of Natural and Applied Sciences, Northwestern Polytechnical University, Xi’an 710129, China
關鍵詞:
喹啉季銨鹽Al2O3Al2O3+CuCl2緩蝕劑復配
Keywords:
quinolone quaternary ammonium saltAl2O3Al2O3+CuCl2corrosion inhibitioncompound
分類號:
TG174.42
DOI:
10.19291/j.cnki.1001-3938.2017.08.002
文獻標志碼:
A
摘要:
為了提高喹啉季銨鹽對N80鋼的緩蝕性能,采用靜態失重法和動電位極化曲線法,研究了在90 ℃、15%HCl溶液中添加Al2O3及Al2O3+CuCl2對喹啉季銨鹽緩蝕性能的影響。試驗結果顯示,160 ℃溫度下合成的喹啉季銨鹽緩蝕效果較差,不能滿足SY/T 5405—1996中的一級指標要求;Al2O3的加入能有效提高喹啉季銨鹽對N80鋼的緩蝕效果,并且能大大降低喹啉季銨鹽的用量;Al2O3+CuCl2和喹啉季銨鹽復配后,能更大程度上提高喹啉季銨鹽的緩蝕效果,緩蝕性能明顯好于Al2O3與喹啉季銨鹽形成的復配緩蝕劑。結果表明,喹啉季銨鹽能與金屬離子形成較為穩定的螯合物,螯合物通過化學作用吸附在掛片表面形成一層致密的銅膜,阻止了腐蝕離子向金屬表面移動,從而表現出較好的緩蝕效果。
Abstract:
In order to increase the corrosion inhibition performance of quinolone quaternary ammonium salt on N80 steel, the effect of Al2O3 and Al2O3+CuCl addition on the corrosion inhibition performance of quinoline quaternary ammonium salt in 15%HCl solution at 90 ℃was investigated, by using static weight loss method and polarization curve method. Test results showed that synthesis of quinoline quaternary ammonium salt corrosion inhibition effect at 160 ℃ is poorer, cannot meet the highest level requirement of SY/T 5405—1996 standard; the addition of Al2O3 can effectively enhance the corrosion inhibition effect of quinoline quaternary ammonium salt for N80 steel, and it can greatly reduce the dosage of quinoline quaternary ammonium salt; the compound of Al2O3+CuCl2 and quinoline quaternary ammonium salt can enhance the corrosion inhibition effect of quinoline quaternary ammonium salt to a greater extent, which is obviously better than that of the complex inhibitor from Al2O3 and quinoline quaternary ammonium salt. The results indicated that quinoline quaternary ammonium salt and metal ion can form stable chelates, the chelates is adsorbed by chemical action to form a dense copper film on the hanging surface, which prevents the corrosion ion from moving to the metal surface, thus showing a better corrosion inhibition effect.

參考文獻/References:

[1] 李謙定,李恒娟,盧永斌. 咪唑啉季銨鹽緩蝕劑的合成及應用性能評價[J]. 西安石油大學學報(自然科學版), 2011,26(2):76-79.
[2] 陳蕊,李善建,馮拉俊. 喹啉緩蝕劑對N80石油管道鋼小孔腐蝕的影響[J]. 焊管,2013,36(11):15-19.
[3] 王紅艷,盧永斌,白方林,等. 一種新型Mannich 堿酸化 緩蝕劑的合成及性能評價[J]. 2013,25(2):133-137.
[4] 雷曉維,張娟濤,白真權. 喹啉季銨鹽酸化緩蝕劑對超級13Cr不銹鋼電化學行為的影響[J]. 腐蝕科學與防護技術,2015,27(4):358-362.
[5] 蔣平,趙力云,萬朝暉,等. 喹啉型季銨鹽緩蝕性能評價[J]. 油田化學,2011,28(2):219-223.
[6] 李恒娟. 高溫鹽酸緩蝕劑合成及應用研究[D]. 西安:西安石油大學,2011.
[7] 梁麗. 季銨鹽型緩蝕劑的合成及性能評價[J]. 化學工程,2010,38(10):235-237.
[8] 李善建,馮拉俊,董曉軍,等. 喹啉與硫脲在含飽和CO2氣井采出水中的協同效應[J]. 天然氣工業,2015(5):90-97.
[9] 李小龍, 張軍平, 畢宗岳, 等.  一種新型復配酸化緩蝕劑對N80鋼的緩蝕性能的影響[J]. 焊管,2016,39(6):5-9.
[10] 曹楚南. 腐蝕電化學[M]. 北京: 化學工業出版社, 1984.
[11] 程玉峰,杜元龍,曹楚南,等. Na2SO4溶液中磷酸環己胺的緩蝕機理及其吸附與脫附行為[J]. 中國腐蝕與防護學報,1997,12(2):142-146.
[12] 梅平,霍松,艾俊哲,等. 雙喹啉季銨鹽在鹽酸體系中的緩蝕性能及協同增效作用研究[J]. 化學與生物工程,2010,27(12):12-14.
[13] 張漫路,趙景茂. 緩蝕劑協同效應與協同機理的研究進展[J]. 中國腐蝕與防護學報,2016, 36(1):1-10.

相似文獻/References:

[1]李小龍,等.一種新型復配酸化緩蝕劑對N80鋼緩蝕性能的影響[J].焊管,2016,39(6):5.[doi:10.19291/j.cnki.1001-3938.2016.06.002]
 LI Xiaolong,ZHANG Junping,BI Zongyue,et al.Influence of the Corrosion Inhibition Performance of a New Composite Acidizing Corrosion Inhibitor to N80 Steel[J].,2016,39(8):5.[doi:10.19291/j.cnki.1001-3938.2016.06.002]

備注/Memo

備注/Memo:
收稿日期:2017-05-08
基金項目:國家科技支撐計劃“高強度耐蝕石油天然氣集輸與輸送用管線鋼生產技術”(項目號2011BAE25B03)。
作者簡介:李小龍(1988—),男,碩士,工程師,主要從事石油管材新產品開發及腐蝕與防護研究。
更新日期/Last Update:
2019手机彩票软件排名